Spray Adhesives

 
With fast tack, long bonding range, and little or no soak-in, 3M™ Super 77™ Multipurpose Spray Adhesive is a versatile tool for bonding lightweight materials that include fabrics, plastics, soft foams, paper, cardboard, and thin gauge metals. 3M™ Hi-Strength 90 Spray Adhesive typically
bonds edge banding in 60 seconds compared to 15-20 minutes for many typical bulk contact
adhesives. Strength increases to an ultimate
230 psi in shear and 25 piw in peel.
 
Product
Description
Spray Width
Bonding Range Surfaces one/ both
(PSI) Shear Initial/ Ultimate
Relative Adhesion
Coverage Sq. Ft./ Container (Typical)
Peel Strength (PIW)
Temp. Resistance
FoamFast 74
 ▪ Fast tack with foam-tearing strength
▪ Soft, non-dimpling glue line
▪ General upholstery foam bonding
▪ Knife edge bonding, boxing, edge turning
1" - 4" variable
N/R/15 min.
40/205
20
120*F (49*C)
260
Repositionable 75
 ▪ Clear "tape-like" holds badges during stitching & patterns prior to cutting
▪ No bleed, stain or wrinkle
1 1/2"
1 hr./3 hrs.
15/65
5
120*F (49*C)
100
Hi-Tack 76
 ▪ Multi-purpose with high temperature resistance
▪ Strong one-surface bonds
1" - 4" variable
10 min./1 hr.
25/100
25
160*F (71*C)
100
Super 77
 ▪ Fast, aggressive tack for bonding many lightweight materials.
1 1/2" - 4" fan
15 min./30 min.
25/160
15
110*F (43*C)
220
Foam 78
 ▪ Bonds most insulation including expanded polystyrene & extruded polystyrene
▪ Fast-drying will not attack foam board.
1" - 4" variable
5 min./15 min.
  
7/67
15-20
140*F (60*C)
100
Spray 80
 ▪ Neoprene-based contact adhesive with plasticizer resistance.
▪ Bond supported vinyl, leather, most rubber, most plastics, laminate & wood.
▪ Resists over 200*F (93*C).
3"
N/R/1 hr.
50/400
35
200*F (93*C)
75/30
Hi-Strength 90
 ▪ High contact bond for decorative laminate.
▪ Adheres polyethylene & polypropylene to wood, metal & more
▪ One minute dry time.
1" - 4" variable
N/R/15 min.
45/230
25
160*F (71*C)
100
Note: The technical information and data on these pages should be considered representative or typical only and should not be used for specification purposes.